Neutral silicone, coloured
Prices for customers after login
Register now and access more than 125,000 products
Neutral silicone is not suitable for adhesive bonding or filling hollow spaces. Complies with building material class B2 in accordance with DIN 4102. Due to the large number of varnish and glazing formulations available, especially on alkyd resin paints and powder-coated aluminium, always carry out your own tests on the area first. Risk of yellowing on contact with white alkyd resin paints cannot be excluded. When hardening, neutral silicone gives off an odour typical of silicone. This odour can no longer be smelled once the hardening process is complete.
For materials and substances that come into contact with the sealant after processing, the user must ensure that their content or fumes cannot cause any impairment or alteration (e.g. discolouration) of the sealant joint. To determine the precise colour, use sample card art. no. 5995000402
No bag tips, art. no. 0891601001, are provided with the 600 ml bags. These must be ordered separately.
Tested in accordance with EN 15651 Part 1 INT
The usage instructions are recommendations based on the tests we have conducted and our experience; carry out your own tests before each application. Due to the large number of applications and storage and processing conditions, we do not assume any liability for a specific application result. Insofar as our free customer service provides technical information or acts as an advisory service, no responsibility is assumed by this service except where the advice or information given falls within the scope of our specified, contractually agreed service or the advisor was acting deliberately. We guarantee consistent quality of our products. We reserve the right to make technical changes and further develop products.
Please observe the "General Notes on Application for Sealants" and "Construction Material Compatibility of Würth Sealants" overview sheet.
Neutral crosslinked silicones, oxime-based
Min. skin-formation time
Continuous motion absorption
Min./max. skin-formation time /conditions
5-8 min / at 23°C and 50% relative humidity
Full curing speed/conditions
2 mm/d / 23°C and 50% relative humidity
Shelf life from production
Min./max. processing temperature
5 to 40 °C
Min./max. temperature resistance
-40 to 150 °C
Recoatable/Can be painted over
Shore A hardness
Min. breaking elongation
Breaking elongation conditions
for 2-mm film
Building material class
B2 - Normally inflammable
Select RAL-colour code
!! NOTE: On-screen visualisation of the colour differs from real colour shade!!