Acrylic fire-retardant joint sealant

Fire protection joint sealer acrylic
FRETRDSEAL-ACRY-B2-WHITE-310ML

Art.-no. 0893303002

Prices for customers after login

Acrylic fire-retardant joint sealant

Art.-no. 0893303002

Prices for customers after login

Quantity

PU

In : currently piece / pieces available

Show availability in Würth branch offices

Exclusively for trade customers

Register now and access more than 125,000 products

Ready-to-use acrylic sealant to close connecting joints between structural and installed parts

  • Designed for easy use on construction sites

  • Building material class B2

  • Neutral odour

  • Resists ageing and weathering

  • Good UV resistance

  • Colour: White, similar to RAL 9003

  • Halogen-free

  • Silicone-free
Notice

The surface must be dry, capable of bearing loads and free of dust or grease


Pre-coat absorbent surfaces with dilute sealing compound (1 to 4 parts water to one part acrylic fire-retardant joint sealant)



The sealant must only be subject to two-side adhesion



Calculate the joint depth to joint width ratio in accordance with DIN 18540



Clean tools with water immediately after use


Fresh sealant can be removed using a damp cloth



Observe general construction test certificate ABP no. P-3786/243/11-MPA BS for use in classified fire protection joints

Application area[G] + J1
  • [G]

  • Joint system A J1


Sealing system for construction joints with low expansion load



F 30–F 90 in accordance with DIN 4102 part 2

Colour

White

Building material class

B2 - Normally inflammable

Min./max. processing temperature

5 to 40 °C

Shelf life from production

24 Month

Contents

310 ml

Chemical basis

Acrylate dispersion

Container

Cartridge

Fully hardening/curing conditions

23°C and 50% relative humidity

Full curing speed

2 mm/d

Conditions to maintain shelf life from production

cool, dry and frost-free storage area

Density

1.56 g/cm³

Min. temperature resistance of the hardened material

-25 °C

Max. temperature resistance of the hardened material

80 °C

Conditions for skin-formation time

at 23°C and 50% relative humidity

Min. skin-formation time

10 min

Stability under load

2 mm

Max. motion absorption (in %)

15 %

Shore A hardness

20

Product weight (per item)

542 g

Max. material shrinkage

16 %

Conditions for material shrinkage

in accordance with ISO 10563

Hazardous Material

Product information

Würth Catalogue

Catalogue page as PDF  | 

Flip catalog

Datasheets()

Datasheets ()

CAD Data  | 

Certificates/Documents

 | 

Technical information